Light emitting device

ABSTRACT

A light emitting device is disclosed. The light emitting device may include a light emitting diode (LED) for emitting light and phosphor adjacent to the LED. The phosphor may be excitable by light emitted by the LED and may include a first compound having a host lattice comprising first ions and oxygen. In one embodiment, the host lattice may include silicon, the copper ions may be divalent copper ions and first compound may have an Olivin crystal structure, a β-K2SO4 crystal structure, a trigonal Glaserite (K 3 Na(SO 4 ) 2 ) or monoclinic Merwinite crystal structure, a tetragonal Ackermanite crystal structure, a tetragonal crystal structure or an orthorhombic crystal structure. In another embodiment, the copper ions do not act as luminescent ions upon excitation with the light emitted by the LED.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 12/491,457 (issued as U.S. pat. No. 8,318,044), filed on Jun. 25, 2009, which is a continuation-in-part of U.S. patent application Ser. No. 11/948,845, filed on Nov. 30, 2007 (issued as U.S. Pat. No. 8,066,909), which is a continuation-in-part of U.S. patent application Ser. No. 11/024,702, filed on Dec. 30, 2004 (issued as U.S. Pat. No. 7,554,129), and claims priority of Korean Patent Application No. 10-2004-0042396, filed on Jun. 10, 2004, which are all hereby incorporated by reference for all purposes as if fully set forth herein.

BACKGROUND OF THE INVENTION

1. Field of the Invention

Embodiments of the present invention relate generally to light emitting devices and, more particularly, to light emitting devices including at least one light-emitting diode and phosphor including lead- and/or copper-containing chemical compounds and converting the wavelength of light.

2. Description of the Related Art

Light emitting devices (LEDs), which used to be used for electronic devices, are now used for automobiles and illumination products. Since light emitting devices have superior electrical and mechanical characteristics, demands for light emitting devices have been increased. In connection to this, interests in white LEDs are increasing as an alternative to fluorescent lamps and incandescent lamps.

In LED technology, solution for realization of white light is proposed variously. Normally, realization of white LED technology is to put the phosphor on the light-emitting diode, and mix the primary emission from the light emitting diode and the secondary emission from the phosphor, which converts the wavelength. For example, as shown in WO 98/05078 and WO 98/12757, use a blue light emitting diode, which is capable of emitting a peak wavelength at 450-490 nm, and YAG group material, which absorbs light from the blue light emitting diode and emits yellowish light (mostly), which may have different wavelength from that of the absorbed light. However, phosphors which are used for white LEDs are usually unstable in the water, vapor or polar solvent, and this unstableness may cause changes in the emitting characteristics of white LED.

SUMMARY OF THE INVENTION

One embodiment exemplarily described herein can be generally characterized as a light emitting device that includes a light emitting diode (LED) for emitting light and a phosphor adjacent to the LED. The phosphor is excitable by light emitted by the LED and may include a first compound having a host lattice comprising first ions, silicon and oxygen. A first portion of the first ions may be substituted by divalent copper ions and the first compound may have one of an Olivin crystal structure, a β-K₂SO₄ crystal structure, a trigonal Glaserite (K₃Na(SO₄)₂) or monoclinic Merwinite crystal structure, a tetragonal Ackermanite crystal structure, a tetragonal crystal structure and an orthorhombic crystal structure.

Another embodiment exemplarily described herein can be generally characterized as a light emitting device that includes a light emitting diode (LED) for emitting light and a phosphor adjacent to the LED. The phosphor is excitable by light emitted by the LED and may include a first compound having a host lattice comprising first ions and oxygen. A first portion of the first ions may be substituted by copper ions and the copper ions do not act as luminescent ions upon excitation with the light emitted by the LED.

BRIEF DESCRIPTION OF THE DRAWINGS

Further embodiments of the invention may be apparent upon consideration of the following detailed description, taken in conjunction with the accompanying drawings, in which like reference characters refer to like parts throughout, and in which:

FIG. 1 shows a side cross-sectional view of an illustrative embodiment of a portion of a chip-type package light emitting device;

FIG. 2 shows a side cross-sectional view of an illustrative embodiment of a portion of a top-type package light emitting device;

FIG. 3 shows a side cross-sectional view of an illustrative embodiment of a portion of a lamp-type package light emitting device;

FIG. 4 shows a side cross-sectional view of an illustrative embodiment of a portion of a light emitting device for high power;

FIG. 5 shows a side cross-sectional view of another illustrative embodiment of a portion of a light emitting device for high power;

FIG. 6 shows emitting spectrum of a light emitting device with luminescent material; and

FIG. 7 shows emitting spectrum of the light emitting device with luminescent material according to another embodiment.

DETAILED DESCRIPTION

Refer to the attached drawing, the wavelength conversion light emitting device is going to be explained in detail, and the light emitting device and the phosphor are separately explained for easiness of explanation as below.

(Light Emitting Device)

FIG. 1 shows a side cross-sectional view of an illustrative embodiment of a portion of a chip-type package light emitting device. The chip-type package light emitting device may comprise at least one light emitting diode and a phosphorescent substance. Electrodes 5 may be formed on both sides of substrate 1. Light emitting diode 6 emitting light may be mounted on one of the electrodes 5. Light emitting diode 6 may be mounted on electrode 5 through electrically conductive paste 9. An electrode of light emitting diode 6 may be connected to electrode pattern 5 via an electrically conductive wire 2.

Light emitting diodes may emit light with a wide range of wavelengths, for example, from ultraviolet light to visible light. In one embodiment, a UV light emitting diode and/or blue light emitting diode may be use.

Phosphor, i.e., a phosphorescent substance, 3 may be placed on the top and side faces of the light emitting diode 6. In some embodiments, the phosphor may include lead- and/or copper containing chemical compounds. In some embodiments, the chemical compounds may comprise aluminates, silicates, antimonates, germanates, germanate-silicates, phosphates, or the like, or a combination thereof. Phosphor 3 converts the wavelength of the light from the light emitting diode 6 to another wavelength or other wavelengths. In one embodiment, the light is in a visible light range after the conversion. Phosphor 3 may be applied to light emitting diode 6 after mixing phosphor 3 with a hardening resin. The hardening resin including phosphor 3 may also be applied to the bottom of light emitting diode 6 after mixing phosphor 3 with electrically conductive paste 9.

The light emitting diode 6 mounted on substrate 1 may be sealed with one or more sealing materials 10. Phosphor 3 may be placed on the top and side faces of light emitting diode 6. Phosphor 3 can also be distributed in the hardened sealing material during the production. Such a manufacturing method is described in U.S. Pat. No. 6,482,664, which is hereby incorporated by reference in its entirety.

Phosphor 3 may comprise one or more lead- and/or copper containing chemical compounds. Phosphor 3 may include one or more single chemical compounds. Each single compound may have an emission peak of, for example, from about 440 nm to about 500 nm, from about 500 nm to about 590 nm, or from about 580 nm to 700 nm Phosphor 3 may include one or more single phosphors, which may have an emission peak as exemplified above.

In regard to light emitting device 40, light emitting diode 6 may emit primary light when light emitting diode 6 receives power from a power supply. The primary light then may stimulate phosphor(s) 3, and phosphor(s) 3 may convert the primary light to a light with longer wavelength(s) (a secondary light). The primary light from the light emitting diode 6 and the secondary light from the phosphors 3 are diffused and mixed together so that a predetermined color of light in visible spectrum may be emitted from light emitting diode 6. In one embodiment, more than one light emitting diodes that have different emission peaks can be mounted together. In some embodiments, a mixture ratio of different phosphors can be adjusted to achieve a desired color of light, color temperature, and CRI.

As described above, if the light emitting diode 6 and the compound(s) included in phosphor 3 are properly controlled then the desired color temperature or specific color coordination can be provided, especially, wide range of color temperature, for example, from about 2,000K to about 8,000K or about 10,000K and/or color rendering index of greater than about 60. In some embodiments, the compound(s) included in the phosphor 3 can be controlled to have a color rendering index between about 50 and about 90. In some embodiments, the compound(s) included in the phosphor 3 can be controlled to have a color rendering index greater than about 90. In some embodiments, the compound(s) included in the phosphor 3 can be controlled to have a color rendering index between about 90 and about 95. Therefore, the light emitting devices exemplarily described herein may be used for electronic devices such as home appliances, stereos, telecommunication devices, and for interior/exterior custom displays. The light emitting devices exemplarily described herein may also be used for automobiles and illumination products because they provide similar color temperatures and CRI to those of the visible light.

FIG. 2 shows a side cross-sectional view of an illustrative embodiment of a portion of a top-type package light emitting device. A top-type package light emitting device may have a similar structure as that of the chip type package light emitting device 40 of FIG. 1. The top-type package device may have reflector 31 which may reflect the light from the light emitting diode 6 to the desire direction.

In top-type package light emitting device 50, more than one light emitting diodes can be mounted. Each of such light emitting diodes may have a different peak wavelength from that of others. Phosphor 3 may comprise a plurality of single compounds with different emission peaks. The proportion of each of such plurality of compounds may be regulated. Such a phosphor may be applied to the light emitting diode and/or uniformly distributed in the hardening material of the reflector 31. As explained more fully below, the phosphor may include lead- and/or copper containing aluminate type compounds, lead- and/or copper containing silicates, lead- and/or copper containing antimonates, lead- and/or copper containing germanates, lead- and/or copper containing germanate-silicates, lead and/or copper containing phosphates, or any combination thereof.

In one embodiment, the light emitting device of the FIG. 1 or FIG. 2 can include a metal substrate, which may have good heat conductivity. Such a light emitting device may easily dissipate the heat from the light emitting diode. Therefore, light emitting devices for high power may be manufactured. If a heat sink is provided beneath the metal substrate, the heat from the light emitting diode may be dissipated more effectively.

FIG. 3 shows a side cross-sectional view of an illustrative embodiment of a portion of a lamp-type package light emitting device. Lamp type light emitting device 60 may have a pair of leads 51, 52, and a diode holder 53 may be formed at the end of one lead. Diode holder 53 may have a shape of cup, and one or more light emitting diodes 6 may provided in the diode holder 53. When a number of light emitting diodes are provided in the diode holder 53, each of them may have a different peak wavelength from that of others. An electrode of light emitting diode 6 may be connected to lead 52 by, for example, electrically conductive wire 2.

Regular volume of phosphor 3, which may be mixed in the epoxy resin, may be provided in diode holder 53. As explained more fully below, phosphor 3 may include lead- and/or copper containing components.

Moreover, the diode holder may include the light emitting diode 6 and the phosphor 3 may be sealed with hardening material such as epoxy resin or silicon resin.

In one embodiment, the lamp type package light emitting device may have more than one pair of electrode pair leads.

FIG. 4 shows a side cross-sectional view of an illustrative embodiment of a portion of a light emitting device for high power. Heat sink 71 may be provided inside of housing 73 of the light emitting device for high power 70, and it may be partially exposed to outside. A pair of lead frames 74 may protrude from housing 73.

One or more light emitting diodes may be mounted directly on one lead frame 74, and an electrode of the light emitting diode 6 and another lead frame 74 may be connected via electrically conductive wire. In another embodiment, one or more light emitting diodes may be mounted directly on the heat sink 71, as opposed to directly on the lead frame 74, via thermally conductive adhesive. Electrically conductive plate 9 may be provided between light emitting diode 6 and lead frame 74. The phosphor 3 may be placed on top and side faces of light emitting diode 6.

FIG. 5 shows a side cross-sectional view of another illustrative embodiment of a portion of a light emitting device for high power.

Light emitting device for high power 80 may have housing 63, which may contain light emitting diodes 6, 7, phosphor 3 arranged on the top and side faces of light emitting diodes 6, 7, one or more heat sinks 61, 62, and one or more lead frames 64. In one embodiment, one or more light emitting diodes 6, 7 may be mounted directly on one or more of the heat sinks 61, 62 via thermally conductive adhesive. In one or more of the lead frames 64. The lead frames 64 may receive power from a power supplier and may protrude from housing 63.

In the light emitting devices for high power 70, 80 in the FIGS. 4 and 5, the phosphor 3 can be added to the paste, which may be provided between heat sink and light emitting devices. A lens may be combined with housing 63, 73.

In a light emitting device for high power, one or more light emitting diodes can be used selectively and the phosphor can be regulated depending on the light emitting diode. As explained more fully below, the phosphor may include lead and/or copper containing components.

A light emitting device for high power may have a radiator (not shown) and/or heat sink(s) Air or a fan may be used to cool the radiator.

The light emitting devices exemplarily described herein are not limited to the structures described above, and the structures can be modified depending on the characteristics of light emitting diodes, phosphor, wavelength of light, and also applications. Moreover, new part can be added to the structures.

Exemplary embodiments of the phosphor 3 are described as follows.

(Phosphor)

According to some embodiments, the phosphor 3 may include one or more lead- and/or copper containing chemical compounds. The phosphor 3 may be excited by UV and/or visible (e.g., blue) light, and emit light due to transitions of the direct type, f-d transitions, or charge transfer transitions. In some embodiments, the lead- and/or copper-containing chemical compounds may be generally characterized as including a host lattice having anions and cations. In some embodiments, at least a portion of the cations are divalent cations. In some embodiments, the divalent cations include alkaline earth ions. In some embodiments, at least a portion of the divalent cations of the host lattice are substituted by divalent lead and/or divalent copper ions.

As mentioned above, conventional luminescent materials and phosphors are generally unstable in water, air humidity, water steam and polar solvents. However, due to a higher covalency and a lower basicity, the substitutionally-incorporated divalent lead and/or divalent copper ions in the host lattice of the chemical compound yields luminescent materials have improved resistance against water, air humidity and polar solvents. Moreover, it will be appreciated that the divalent lead and/or divalent copper ions within the host lattice do not act as activators (also referred to herein as “luminescent center ions”) and, therefore do not luminesce.

As described above, the phosphor 3 may include one or more chemical compounds such as, for example, aluminates, silicates, antimonates, germanates, germanate-silicates, and/or phosphates. Exemplary embodiments of these chemical compounds are described in greater detail below.

In some embodiments, the lead- and/or copper-containing aluminates may be generally characterized according to formulas (1), (2), and (5) a(M′O).b(M″₂O).c(M″X).d(Al₂O₃).e(M′″O).f(M″″₂O₃).g(M″″′_(o)O_(p)).h(M″″″_(x)O_(y))  (1)

wherein M′ may be Pb, Cu, and/or any combination thereof; M″ may be one or more monovalent elements, for example, Li, Na, K, Rb, Cs, Au, Ag, and/or any combination thereof; M″′ may be one or more divalent elements, for example, Be, Mg, Ca, Sr, Ba, Zn, Cd, Mn, and/or any combination thereof; M″″ may be one or more trivalent elements, for example, Sc, B, Ga, In, and/or any combination thereof; M″″′ may be Si, Ge, Ti, Zr, Mn, V, Nb, Ta, W, Mo, and/or any combination thereof; M″″″ may be Bi, Sn, Sb, Sc, Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and/or any combination thereof, X may be F, Cl, Br, I, and/or any combination thereof; 0<a≦2; 0≦b≦2; 0≦c≦2; 0<d≦8; 0<e≦4; 0≦f≦3; 0≦g≦8; 0<h≦2; 1≦o≦2; 1≦p≦5; 1≦x≦2; and 1≦y≦5. a(M′O)b(M″₂O)c(M″X)4-a-b-c(M″′O)7(Al₂O₃)d(B₂O₃)e(Ga₂O₃)f(SiO₂)g(GeO₂)h(M″″_(x)O_(y))  (2)

wherein M′ may be Pb, Cu, and/or any combination thereof; M″ may be one or more monovalent elements, for example, Li, Na, K, Rb, Cs, Au, Ag, and/or any combination thereof; M″′ may be one or more divalent elements, for example, Be, Mg, Ca, Sr, Ba, Zn, Cd, Mn, and/or any combination thereof; M″″ may be Bi, Sn, Sb, Sc, Y, La, In, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and any combination thereof, X may be F, Cl, Br, I, and any combination thereof; 0<a≦4; 0≦b≦2; 0≦c≦2; 0≦d≦1; 0≦e≦1; 0≦f≦1; 0≦g≦1; 0<h≦2; 1≦x≦2; and 1≦y≦5.

The preparation of copper- as well as lead containing luminescent materials may be a basic solid state reaction. Pure starting materials without any impurities, e.g. iron, may be used.

Any starting material which may transfer into oxides via a heating process may be used to form oxygen dominated phosphors.

EXAMPLES OF PREPARATION

Preparation of the Luminescent Material Having Formula (3) Cu_(0.02)Sr_(3.98)Al₁₄O₂₅: Eu  (3)

Starting materials: CuO, SrCO₃, Al(OH)₃, Eu₂O₃, and/or any combination thereof.

The starting materials in the form of oxides, hydroxides, and/or carbonates may be mixed in stoichiometric proportions together with small amounts of flux, e.g., H₃BO₃. The mixture may be fired in an alumina crucible in a first step at about 1,200° C. for about one hour. After milling the pre-fired materials a second firing step at about 1,450° C. in a reduced atmosphere for about 4 hours may be followed. After that the material may be milled, washed, dried and sieved. The resulting luminescent material may have an emission maximum of about 494 nm

TABLE 1 copper-containing Eu²⁺-activated aluminate compared with Eu²⁺-activated aluminate without copper at about 400 nm excitation wavelength Copper doped Compound without compound copper Cu_(0.02)Sr_(3.98)Al₁₄O₂₅: Sr₄Al₁₄O₂₅: Eu Eu Luminous 103.1 100 density (%) Wavelength 494 493 (nm)

Preparation of the Luminescent Material Having Formula (4) Pb_(0.05)Sr_(3.95)Al₁₄O₂₅: Eu  (4)

Starting materials: PbO, SrCO₃, Al₂O₃, Eu₂O₃, and/or any combination thereof.

The starting materials in form of very pure oxides, carbonates, or other components which may decompose thermally into oxides, may be mixed in stoichiometric proportion together with small amounts of flux, for example, H₃BO₃. The mixture may be fired in an alumina crucible at about 1,200° C. for about one hour in the air. After milling the pre-fired materials a second firing step at about 1,450° C. in air for about 2 hours and in a reduced atmosphere for about 2 hours may be followed. Then the material may be milled, washed, dried, and sieved. The resulting luminescent material may have an emission maximum of from about 494.5 nm

TABLE 2 lead-containing Eu²⁺-activated aluminate compared with Eu²⁺-activated aluminate without lead at about 400 nm excitation wavelength Lead-containing Compound without compound lead Pb_(0.05)Sr_(3.95)Al₁₄O₂₅: Sr₄Al₁₄O₂₅: Eu Eu Luminous 101.4 100 density (%) Wavelength 494.5 493 (nm)

TABLE 3 optical properties of some copper- and/or lead doped aluminates excitable by long wave ultraviolet and/or by visible light and their luminous density in % at 400 nm excitation wavelength Luminous density at 400 nm excitation Peak wave length of Possible compared with compounds lead-/copper- Peak wave length of excitation not containing contaning materials without Composition range(nm) copper/lead (%) materials (nm) lead/copper (nm) Cu_(0.5)S_(r3.5)Al₁₄O₂₅: Eu 360-430 101.2 495 493 Cu_(0.02)Sr_(3.98)Al₁₄O₂₅: Eu 360-430 103.1 494 493 Pb_(0.05)Sr_(3.95)Al₁₄O₂₅: Eu 360-430 101.4 494.5 493 Cu_(0.01)Sr_(3.99)Al_(13.995)Si_(0.005)O₂₅: Eu 360-430 103 494 492 Cu_(0.01)Sr_(3.395)Ba_(0.595)Al₁₄O₂₅: Eu, Dy 360-430 100.8 494 493 Pb_(0.05)Sr_(3.95)Al_(13.95)Ga_(0.05)O₂₅: Eu 360-430 101.5 494 494 a(M′O).b(M″O).c(Al₂O₃).d(M″′₂O₃).e(M″″O₂).f(M″″′_(x)O_(y))  (5)

wherein M′ may be Pb, Cu, and/or any combination thereof; M″ may be Be, Mg, Ca, Sr, Ba, Zn, Cd, Mn, and/or any combination thereof; M″′ may be B, Ga, In, and/or any combination thereof; M″″ may be Si, Ge, Ti, Zr, Hf, and/or any combination thereof; M″″′ may be Bi, Sn, Sb, Sc, Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and/or any combination thereof; 0<a≦1; 0≦b≦2; 0<c≦8; 0≦d≦1; 0≦e≦1; 0<f≦2; 1≦x≦2; and 1≦y≦5.

EXAMPLE OF PREPARATION

Preparation of the Luminescent Material Having Formula (6) Cu_(0.05)Sr_(0.95)Al_(1.9997)Si_(0.0003)O₄: Eu  (6)

Starting materials: CuO, SrCO₃, Al₂0₃, SiO₂, Eu₂O₃, and/or any combination thereof.

The starting materials in the form of, for example, pure oxides and/or as carbonates may be mixed in stoichiometric proportions together with small amounts of flux, for example, AlF₃. The mixture may be fired in an alumina crucible at about 1,250° C. in a reduced atmosphere for about 3 hours. After that the material may be milled, washed, dried and sieved. The resulting luminescent material may have an emission maximum of about 521.5 nm

TABLE 4 copper-containing Eu²⁺-activated aluminate compared with Eu²⁺-activated aluminate without copper at about 400 nm excitation wavelength Copper-containing Compound without compound copper Cu_(0.05)Sr_(0.95)Al_(1.9997)Si_(0.0003)O₄: SrAl₂O₄: Eu Eu Luminous 106 100 density (%) Wavelength 521.5 519 (nm)

Preparation of the Luminescent Material Having Formula (7) Cu_(0.12)BaMg_(1.88)Al₁₆O₂₇: Eu  (7)

Starting materials: CuO, MgO, BaCO₃, Al(OH)₃, Eu₂O₃, and/or any combination thereof.

The starting materials in the form of, for example, pure oxides, hydroxides, and/or carbonates may be mixed in stoichiometric proportions together with small amounts of flux, for example, AlF₃. The mixture may be fired in an alumina crucible at about 1,420° C. in a reduced atmosphere for about 2 hours. After that the material may be milled, washed, dried, and sieved. The resulting luminescent material may have an emission maximum of about 452 nm

TABLE 5 copper-containing Eu²⁺-activated aluminate compared with copper not doped Eu²⁺-activated aluminate at 400 nm excitation wavelength Copper-containing Comparison without compound copper Cu_(0.12)BaMg_(1.88)A1₁₆O₂₇: BaMg₂A1₁₆O₂₇: Eu Eu Luminous 101 100 density (%) Wavelength 452 450 (nm)

Preparation of the Luminescent Material Having Formula (8) Pb_(0.1)Sr_(0.9)Al₂O₄: Eu  (8)

Starting materials: PbO, SrCO₃, Al(OH)₃, Eu₂O₃, and/or any combination thereof.

The starting materials in form of, for example, pure oxides, hydroxides, and/or carbonates may be mixed in stoichiometric proportions together with small amounts of flux, for example, H₃BO₃. The mixture may be fired in an alumina crucible at about 1,000° C. for about 2 hours in the air. After milling the pre-fired materials a second firing step at about 1,420° C. in the air for about 1 hour and in a reduced atmosphere for about 2 hours may be followed. After that the material may be milled, washed, dried and sieved. The resulting luminescent material may have an emission maximum of about 521 nm

TABLE 6 lead-containing Eu²⁺-activated aluminate compared with Eu²⁺-activated aluminate without lead at about 400 nm excitation wavelength Lead-containing Compound without compound lead Pb_(0.1)Sr_(0.9)Al₂O₄: SrAl₂O₄: Eu Eu Luminous 102 100 density (%) Wavelength 521 519 (nm)

Results obtained in regard to copper- and/or lead doped aluminates are shown in table 7.

TABLE 7 optical properties of some copper- and/or lead doped aluminates excitable by long wave ultraviolet and/or by visible light and their luminous density in % at 400 nm excitation wavelength Luminous density at 400 nm excitation Peak wave length of Possible compared with compounds lead-/copper- Peak wave length of excitation not containing containing materials without Composition range (nm) copper/lead (%) materials (nm) lead/copper (nm) Cu_(0.05)S_(r0.95)A1_(1.9997)Si_(0.0003)O₄: Eu 360-440 106   521.5 519 Cu_(0.2)Mg_(0.7995)Li_(0.0005)Al_(1.9)Ga_(0.1)O₄: Eu, Dy 360-440 101.2 482 480 Pb_(0.1)Sr_(0.9)Al₂O₄: Eu 360-440 102 521 519 Cu_(0.05)BaMg_(1.95)Al₁₆O₂₇: Eu, Mn 360-400 100.5 451, 515 450, 515 Cu_(0.12)BaMg_(1.88)Al₁₆O₂₇: Eu 360-400 101 452 450 Cu_(0.01)BaMg_(0.99)Al₁₀O₁₇: Eu 360-400 102.5 451 449 Pb_(0.1)BaMg_(0.9)Al_(9.5)Ga_(0.5)O₁₇: Eu, Dy 360-400 100.8 448 450 Pb_(0.08)Sr_(0.902)Al₂O₄: Eu, Dy 360-440 102.4 521 519 Pb_(0.2)Sr_(0.8)Al₂O₄: Mn 360-440 100.8 658 655 Cu_(0.06)Sr_(0.94)Al₂O₄: Eu 360-440 102.3 521 519 Cu_(0.05)Ba_(0.94)Pb_(0.06)Mg_(0.95)Al₁₀O₁₇: Eu 360-440 100.4 451 449 Pb_(0.3)Ba_(0.7)Cu_(0.1)Mg_(1.9)Al₁₆O₂₇: Eu 360-400 100.8 452 450 Pb_(0.3)Ba_(0.7)Cu_(0.1)Mg_(1.9)Al₁₆O₂₇: Eu, Mn 360-400 100.4 452, 515 450, 515

In some embodiments, the lead- and/or copper-containing silicates may be generally characterized according to formula (9) a(M′O).b(M″O).c(M″′X).d(M″′₂O).e(M″″₂O₃).f(M″″′_(o)O_(p)).g(SiO₂).h(M″″″″_(x)O_(y))  (9)

wherein M′ may be Pb, Cu, and/or any combination thereof; M″ may be Be, Mg, Ca, Sr, Ba, Zn, Cd, Mn, and/or any combination thereof; M″′ may be Li, Na, K, Rb, Cs, Au, Ag, and/or any combination thereof; M″″ may be Al, Ga, In, and/or any combination thereof; M″″′ may be Ge, V, Nb, Ta, W, Mo, Ti, Zr, Hf, and/or any combination thereof; M″″″ may be Bi, Sn, Sb, Sc, Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, and/or any combination thereof; X may be F, Cl, Br, I, and any combination thereof; 0<a≦2; 0<b≦8; 0≦c≦4; 0≦d≦2; 0≦e≦2; 0≦f≦2; 0<g≦10; 0<h≦5; 1≦o≦2; 1≦p≦5; 1≦x≦2; and 1≦y≦5.

The copper-containing silicates exemplarily described herein may, in some embodiments, contain SiO₄ and can be characterized as having an Olivin structure (orthorhombic) or β-K₂SO₄ structure (orthorhombic); contain Si₂O₈ and be characterized as having a trigonal Glaserite (K₃Na(SO₄)₂) or monoclinic Merwinite structure; contain Si₂O₇ and be characterized as having a tetragonal Ackermanite structure; contain SiO₅ and be characterized as having a tetragonal structure; and/or contain Si₂O₅ and be characterized as having an orthorhombic structure.

EXAMPLE OF PREPARATION

Preparation of the Luminescent Material Having Formula (10) Cu_(0.05)Sr_(1.7)Ca_(0.25)SiO₄: Eu  (10)

Starting materials: CuO, SrCO₃, CaCO₃, SiO₂, Eu₂O₃, and/or any combination thereof.

The starting materials in the form of pure oxides and/or carbonates may be mixed in stoichiometric proportions together with small amounts of flux, for example NH₄Cl. The mixture may be fired in an alumina crucible at about 1,200° C. in an inert gas atmosphere (e.g., N₂ or noble gas) for about 2 hours. Then the material may be milled. After that, the material may be fired in an alumina crucible at about 1,200° C. in a slightly reduced atmosphere for about 2 hours. Then, the material may be milled, washed, dried, and sieved. The resulting luminescent material may have an emission maximum at about 592 nm

TABLE 8 copper-containing Eu²⁺-activated silicate compared with Eu²⁺-activated silicate without copper at about 400 nm excitation wavelength Copper-containing Compound without compound copper Cu_(0.05)Sr_(1.17)Ca_(0.25)SiO₄: Sr_(1.7)Ca_(0.3)SiO₄: Eu Eu Luminous 104 100 density (%) Wavelength 592 588 (nm)

Preparation of the Luminescent Material Having Formula (11): Cu_(0.2)Ba₂Zn_(0.2)Mg_(0.6)Si₂O₇: Eu  (11)

Starting materials: CuO, BaCO₃, ZnO, MgO, SiO₂, Eu₂O₃, and/or any combination thereof.

The starting materials in the form of very pure oxides and carbonates may be mixed in stoichiometric proportions together with small amounts of flux, for example, NH₄Cl. In a first step the mixture may be fired in an alumina crucible at about 1,100° C. in a reduced atmosphere for about 2 hours. Then the material may be milled. After that the material may be fired in an alumina crucible at about 1,235° C. in a reduced atmosphere for about 2 hours. Then that the material may be milled, washed, dried and sieved. The resulting luminescent material may have an emission maximum at about 467 nm.

TABLE 9 copper-containing Eu²⁺-activated silicate compared with Eu²⁺-activated silicate without copper at 400 nm excitation wavelength Copper-containing Compound without compound copper Cu_(0.2)Sr₂Zn_(0.2)Mg_(0.6)Si₂O₇: Sr₂Zn₂Mg_(0.6)Si₂O₇: Eu Eu Luminous 101.5 100 density (%) Wavelength 467 465 (nm)

Preparation of the Luminescent Material Having Formula (12) Pb_(0.1)Ba_(0.95)Sr_(0.95)Si_(0.998)Ge_(0.002)O₄: Eu  (12)

Starting materials: PbO, SrCO₃, BaCO₃, SiO₂, GeO₂, Eu₂O₃, and/or any combination thereof.

The starting materials in the form of oxides and/or carbonates may be mixed in stoichiometric proportions together with small amounts of flux, for example, NH₄Cl. The mixture may be fired in an alumina crucible at about 1,000° C. for about 2 hours in the air. After milling the pre-fired materials a second firing step at 1,220° C. in air for 4 hours and in reducing atmosphere for 2 hours may be followed. After that the material may be milled, washed, dried and sieved. The resulting luminescent material may have an emission maximum at about 527 nm.

TABLE 10 lead-containing Eu²⁺-activated silicate compared with Eu²⁺-activated silicate without lead at about 400 nm excitation wavelength Lead-containing Compound without compound lead Pb_(0.1)Ba_(0.95)Sr_(0.95)Si_(0.998)Ge_(0.002)O₄: BaSrSiO₄: Eu Eu Luminous 101.3 100 density (%) Wavelength 527 525 (nm)

Preparation of the Luminescent Material Having Formula (13) Pb_(0.25)Sr_(3.75)Si₃O₈Cl₄: Eu  (13)

Starting materials: PbO, SrCO₃, SrCl₂ SiO₂, Eu₂O₃, and any combination thereof.

The starting materials in the form of oxides, chlorides, and/or carbonates may be mixed in stoichiometric proportions together with small amounts of flux, for example, NH₄Cl. The mixture may be fired in an alumina crucible in a first step at about 1,100° C. for about 2 hours in the air. After milling the pre-fired materials a second firing step at about 1,220° C. in the air for about 4 hours and in a reduced atmosphere for about 1 hour may be followed. After that the material may be milled, washed, dried and sieved. The resulting luminescent material may have an emission maximum at about 492 nm

TABLE 11 lead-containing Eu²⁺-activated chlorosilicate compared with Eu²⁺-activated chlorosilicate without lead at 400 nm excitation wavelength Lead-containing Compound without compound lead Pb_(0.25)Sr_(3.75)Si₃O₈Cl₄: Sr₄Si₃O₈Cl₄: Eu Eu Luminous 100.6 100 density (%) Wavelength 492 490 (nm)

Results obtained with respect to copper- and/or lead-containing silicates are shown in table 12.

TABLE 12 optical properties of some copper- and/or lead-containing rare earth activated silicates excitable by long wave ultraviolet and/or by visible light and their luminous density in % at about 400 nm excitation wavelength Luminous density at 400 nm excitation Peak wave length of Possible compared with compounds lead-/copper- Peak wave length of excitation not containing doped materials without Composition range (nm) copper/lead (%) materials (nm) lead/copper (nm) Pb_(0.1)Ba_(0.95)S_(r0.95)Si_(0.998)Ge_(0.002)O₄: Eu 360-470 101.3 527 525 Cu_(0.02)(Ba,Sr,Ca,Zn)_(1.98)SiO₄: Eu 360-500 108.2 565 560 Cu_(0.05)Sr_(1.7)Ca_(0.25)SiO₄: Eu 360-470 104 592 588 Cu_(0.05)Li_(0.002)Sr_(1.5)Ba_(0.448)SiO₄: Gd, Eu 360-470 102.5 557 555 Cu_(0.2)Sr₂Zn_(0.2)Mg_(0.6)Si₂O₇: Eu 360-450 101.5 467 465 Cu_(0.02)Ba_(2.8)Sr_(0.2)Mg_(0.98)Si₂O₈: Eu, Mn 360-420 100.8 440, 660 438, 660 Pb_(0.25)Sr_(3.75)Si₃O₈Cl₄: Eu 360-470 100.6 492 490 Cu_(0.2)Ba_(2.2)Sr_(0.75)Pb_(0.05)Zn_(0.8)Si₂O₈: Eu 360-430 100.8 448 445 Cu_(0.2)Ba₃Mg_(0.8)Si_(1.99)Ge_(0.01)O₈: Eu 360-430 101 444 440 Cu_(0.5)Zn_(0.5)Ba₂Ge_(0.2)Si_(1.8)O₇: Eu 360-420 102.5 435 433 Cu_(0.8)Mg_(0.2)Ba₃Si₂O₈: Eu, Mn 360-430 103 438, 670 435, 670 Pb_(0.15)Ba_(1.84)Zn_(0.01)Si_(0.99)Zr_(0.01)O₄: Eu 360-500 101 512 510 Cu_(0.2)Ba₅Ca_(2.8)Si₄O₁₆: Eu 360-470 101.8 495 491

In some embodiments, the lead- and/or copper-containing antimonates may be generally characterized according to formula (14) a(M′O).b(M″₂O).c(M″X).d(Sb₂O₅).e(M″′O).f(M″″_(x)O_(y))  (14)

wherein M′ may be Pb, Cu, and/or any combination thereof; M″ may be Li, Na, K, Rb, Cs, Au, Ag, and/or any combination thereof; M″′ may be Be, Mg, Ca, Sr, Ba, Zn, Cd, Mn, and/or any combination thereof; M″″ may be Bi, Sn, Sc, Y, La, Pr, Sm, Eu, Tb, Dy, Gd, and/or any combination thereof; X may be F, Cl, Br, I, and/or any combination thereof; 0<a≦2; 0≦b≦2; 0≦c≦4; 0<d≦8; 0≦e≦8; 0≦f≦2; 1≦x≦2; and 1≦y≦5.

EXAMPLES OF PREPARATION

Preparation of the Luminescent Material Having Formula (15) Cu_(0.2)Mg_(1.7)Li_(0.2)Sb₂O₇: Mn  (15)

Starting materials: CuO, MgO, Li₂O, Sb₂O₅, MnCO₃, and/or any combination thereof.

The starting materials in the form of oxides may be mixed in stoichiometric proportion together with small amounts of flux. In a first step the mixture may be fired in an alumina crucible at about 985° C. in the air for about 2 hours. After pre-firing the material may be milled again. In a second step the mixture may be fired in an alumina crucible at about 1,200° C. in an atmosphere containing oxygen for about 8 hours. After that the material may be milled, washed, dried and sieved. The resulting luminescent material may have an emission maximum at about 626 nm

TABLE 13 copper-containing antimonate compared with antimonate without copper at about 400 nm excitation wavelength Copper-containing Comparison without compound copper Cu_(0.2)Mg_(1.7)Li_(0.2)Sb₂O₇: Mg₂Li_(0.2)Sb₂O₇: Mn Mn Luminous 101.8 100 density (%) Wavelength 652 650 (nm)

Preparation of the Luminescent Material Having Formula (16) Pb_(0.006)Ca_(0.6)Sr_(0.394)Sb₂O₆  (16)

Starting materials: PbO, CaCO₃, SrCO₃, Sb₂O₅, and/or any combination thereof.

The starting materials in the form of oxides and/or carbonates may be mixed in stoichiometric proportions together with small amounts of flux. In a first step the mixture may be fired in an alumina crucible at about 975° C. in the air for about 2 hours. After pre-firing the material may be milled again. In a second step the mixture may be fired in an alumina crucible at about 1,175° C. in the air for about 4 hours and then in an oxygen-containing atmosphere for about 4 hours. After that the material may be milled, washed, dried and sieved. The resulting luminescent material may have an emission maximum at about 637 nm

TABLE 14 lead-containing antimonate compared with antimonate without lead at 400 nm excitation wavelength Lead-containing Compound without compound lead Pb_(0.006)Ca_(0.6)Sr_(0.394)Sb₂O₆ Ca_(0.6)Sr_(0.4)Sb₂O₆ Luminous 102 100 density (%) Wavelength 637 638 (nm)

Results obtained in respect to copper- and/or lead-containing antimonates are shown in table 15.

TABLE 15 optical properties of some copper- and/or lead-containing antimonates excitable by long wave ultraviolet and/or by visible light and their luminous density in % at about 400 nm excitation wavelength Luminous density at 400 nm excitation Peak wave length of Possible compared compounds lead-/copper- Peak wave length of excitation not containing doped materials without Composition range (nm) copper/lead (%) materials (nm) lead/copper (nm) Pb_(0.2)Mg_(0.002)Ca_(1.798)Sb₂O₆F₂: Mn 360-400 102 645 649 Cu_(0.15)Ca_(1.845)Sr_(0.005)Sb_(1.998)Si_(0.002)O₇: Mn 360-400 101.5 660 658 Cu_(0.2)Mg_(1.7)Li_(0.2)Sb₂O₇: Mn 360-400 101.8 652 650 Cu_(0.2)Pb_(0.01)Ca_(0.79)Sb_(1.98)Nb_(0.02)O₆: Mn 360-400 98.5 658 658 Cu_(0.01)Ca_(1.99)Sb_(1.9995)V_(0.0005)O₇: Mn 360-400 100.5 660 657 Pb_(0.006)Ca_(0.6)Sr_(0.394)Sb₂O₆ 360-400 102 637 638 Cu_(0.02)Ca_(0.9)Sr_(0.5)Ba_(0.4)Mg_(0.18)Sb₂O₇ 360-400 102.5 649 645 Pb_(0.198)Mg_(0.004)Ca_(1.798)Sb₂O₆F₂ 360-400 101.8 628 630

In some embodiments, the lead- and/or copper-containing germanates and/or germanate-silicates may be generally characterized according to formula (17) a(M′O).b(M″₂O)c(M″X).d(GeO₂).e(M″′O).f(M″″₂O₃).g(M″″′_(o)O_(p)).h(M″″″_(x)O_(y))  (17)

wherein M′ may be Pb, Cu, and/or any combination thereof; M″ may be Li, Na, K, Rb, Cs, Au, Ag, and/or any combination thereof; M″′ may be Be, Mg, Ca, Sr, Ba, Zn, Cd, and/or any combination thereof; M″″ may be Sc, Y, B, Al, La, Ga, In, and/or any combination thereof; M″″′ may be Si, Ti, Zr, Mn, V, Nb, Ta, W, Mo, and/or any combination thereof; M″″″ may be Bi, Sn, Pr, Sm, Eu, Gd, Dy, and/or any combination thereof X may be F, Cl, Br, I, and/or any combination thereof 0<a≦2; 0≦b≦2; 0≦c≦10; 0<d≦10; 0≦e≦14; 0≦f≦14; 0≦g≦10; 0≦h≦2; 1≦o≦2; 1≦p≦5; 1≦x≦2; and 1≦y≦5.

EXAMPLE OF PREPARATION

Preparation of the Luminescent Material Having Formula (18) Pb_(0.004)Ca_(1.99)Zn_(0.006)Ge_(0.8)Si_(0.2)O₄: Mn  (18)

Starting materials: PbO, CaCO₃, ZnO, GeO₂, SiO₂, MnCO₃, and/or any combination thereof,

The starting materials in the form of oxides and/or carbonates may be mixed in stoichiometric proportions together with small amounts of flux, for example, NH₄Cl. In a first step the mixture may be fired in an alumina crucible at about 1,200° C. in an oxygen-containing atmosphere for about 2 hours. Then, the material may be milled again. In a second step the mixture may be fired in an alumina crucible at about 1,200° C. in oxygen containing atmosphere for about 2 hours. After that the material may be milled, washed, dried and sieved. The resulting luminescent material may have an emission maximum at about 655 nm.

TABLE 16 lead-containing Mn-activated germanate compared with Mn-activated germanate without lead at about 400 nm excitation wavelength Copper-containing Comparison without compound copper Pb_(0.004)Ca_(1.99)Zn_(0.006)Ge_(0.8)Si_(0.2)O₄: Ca_(1.99)Zn_(0.01)Ge_(0.8)Si_(0.2)O₄: Mn Mn Luminous 101.5 100 density (%) Wavelength 655 657 (nm)

Preparation of the Luminescent Material Having Formula (19) Cu_(0.46)Sr_(0.54)Ge_(0.6)Si_(0.4)O₃: Mn  (19)

Starting materials: CuO, SrCO₃, GeO₂, SiO₂, MnCO₃, and/or any combination thereof.

The starting materials in the form of oxides and/or carbonates may be mixed in stoichiometric proportions together with small amounts of flux, for example, NH₄Cl. In a first step the mixture may be fired in an alumina crucible at about 1,100° C. in an oxygen-containing atmosphere for about 2 hours. Then, the material may be milled again. In a second step the mixture may be fired in an alumina crucible at about 1,180° C. in an oxygen-containing atmosphere for about 4 hours. After that the material may be milled, washed, dried and sieved. The resulting luminescent material may have an emission maximum at about 658 nm.

TABLE 17 copper-containing Mn-activated germanate-silicate compared with Mn-activated germanate-silicate without copper at 400 nm excitation wavelength Copper-containing Compound without compound copper Cu_(0.46)Sr_(0.54)Ge_(0.6)Si_(0.4)O₃: SrGe_(0.6)Si_(0.4)O₃: Mn Mn Luminous 103 100 density (%) Wavelength 658 655 (nm)

TABLE 18 optical properties of some copper- and/or lead-doped germanate-silicates excitable by long wave ultraviolet and/or by visible light and their luminous density in % at about 400 nm excitation wavelength Luminous density at 400 nm excitation Peak wave length of Possible compared with compounds lead-/copper- Peak wave length of excitation not containing doped materials without Composition range (nm) copper/lead (%) materials (nm) lead/copper (nm) Pb_(0.004)Ca_(1.99)Zn_(0.006)Ge_(0.8)Si_(0.2)O₄: Mn 360-400 101.5 655 657 Pb_(0.002)Sr_(0.954)Ca_(1.044)Ge_(0.93)Si_(0.07)O₄: Mn 360-400 101.5 660 661 Cu_(0.46)Sr_(0.54)Ge_(0.6)Si_(0.4)O₃: Mn 360-400 103 658 655 Cu_(0.002)Sr_(0.998)Ba_(0.99)Ca_(0.01)Si_(0.98)Ge_(0.02)O₄: Eu 360-470 102 538 533 Cu_(1.45)Mg_(26.55)Ge_(9.4)Si_(0.6)O₄₈: Mn 360-400 102 660 657 Cu_(1.2)Mg_(26.8)Ge_(8.9)Si_(1.1)O₄₈: Mn 360-400 103.8 670 656 Cu₄Mg₂₀Zn₄Ge₅Si_(2.5)O₃₈F₁₀: Mn 360-400 101.5 658 655 Pb_(0.001)Ba_(0.849)Zn_(0.05)Sr_(1.1)Ge_(0.04)Si_(0.96)O₄: Eu 360-470 101.8 550 545 Cu_(0.05)Mg_(4.95)GeO₆F₂: Mn 360-400 100.5 655 653 Cu_(0.05)Mg_(3.95)GeO_(5.5)F: Mn 360-400 100.8 657 653

In some embodiments, the lead- and/or copper-containing phosphates may be generally characterized according to formula (20) a(M′O).b(M″₂O).c(M″X).d(P₂O₅).e(M″′O).f(M″″₂O₃).g(M″″′O₂).h(M″″″_(x)O_(y))  (20)

wherein M′ may be Pb, Cu, and/or any combination thereof; M″ may be Li, Na, K, Rb, Cs, Au, Ag, and/or any combination thereof; M″′ may be Be, Mg, Ca, Sr, Ba, Zn, Cd, Mn, and/or any combination thereof; M″″ may be Sc, Y, B, Al, La, Ga, In, and/or any combination thereof; M″″′ may be Si, Ge, Ti, Zr, Hf, V, Nb, Ta, W, Mo, and/or any combination thereof; M″″″ may be Bi, Sn, Pr, Sm, Eu, Gd, Dy, Ce, Th, and/or any combination thereof, X may be F, Cl, Br, I, and/or any combination thereof; 0<a≦2; 0≦b≦12; 0≦c≦16; 0<d≦3; 0≦e≦5; 0≦f≦3; 0≦g≦2; 0<h≦2; 1≦x≦2; and 1≦y≦5.

EXAMPLES OF PREPARATION

Preparation of the Luminescent Material Having Formula (21) Cu_(0.02)Ca_(4.98)(PO₄)₃Cl: Eu  (21)

Starting materials: CuO, CaCO₃, Ca₃(PO₄)₂, CaCl₂, Eu₂O₃, and/or any combination thereof,

The starting materials in the form of oxides, phosphates, and/or carbonates and chlorides may be mixed in stoichiometric proportions together with small amounts of flux. The mixture may be fired in an alumina crucible at about 1,240° C. in reducing atmosphere for about 2 hours. After that the material may be milled, washed, dried and sieved. The luminescent material may have an emission maximum at about 450 nm.

TABLE 19 copper-containing doped Eu²⁺-activated chlorophosphate compared with Eu²⁺-activated chlorophosphate without copper at about 400 nm excitation wavelength Copper-containing Compound without compound copper Cu_(0.02)Ca_(4.98)(PO₄)₃Cl: Ca₅(PO₄)₃Cl: Eu Eu Luminous 101.5 100 density (%) Wavelength 450 447 (nm)

TABLE 20 copper- and/or lead-containing phosphates excitable by long wave ultraviolet and/or by visible light and their luminous density in % at about 400 nm excitation wavelength Luminous density at 400 nm excitation Peak wave length of Possible compared with compounds lead-/copper- Peak wave length of excitation not containing doped materials without Composition range (nm) copper/lead (%) materials (nm) lead/copper (nm) Cu_(0.02)Sr_(4.98)(PO₄)₃Cl: Eu 360-410 101.5 450 447 Cu_(0.2)Mg_(0.8)BaP₂O₇: Eu, Mn 360-400 102 638 635 Pb_(0.5)Sr_(1.5)P_(1.84)B_(0.16)O_(6.84): Eu 360-400 102 425 420 Cu_(0.5)Mg_(0.5)Ba₂(P,Si)₂O₈: Eu 360-400 101 573 570 Cu_(0.5)Sr_(9.5)(P,B)₆O₂₄Cl₂: Eu 360-410 102 460 456 Cu_(0.5)Ba₃Sr_(6.5)P₆O₂₄(F,Cl)₂: Eu 360-410 102 443 442 Cu_(0.05)(Ca,Sr,Ba)_(4.95)P₃O₁₂Cl: Eu, Mn 360-410 101.5 438, 641 435, 640 Pb_(0.1)Ba_(2.9)P₂O₈: Eu 360-400 103 421 419

Meanwhile, the phosphor of the light emitting device can comprise aluminate, silicate, antimonate, germanate, phosphate type chemical compound, and any combination thereof.

FIG. 6 is one of the embodiment's emission spectrum according to the invention, which the phosphor is used for the light emitting device. The embodiment may have a light emitting diode with 405 nm wavelength and the phosphor, which is mixture of the selected multiple chemical compounds in proper ratio. The phosphor may be composed of Cu_(0.05)BaMg_(1.95)Al₁₆O₂₇: Eu which may have peak wavelength at about 451 nm, Cu_(0.03)Sr_(1.5)Ca_(0.47)SiO₄: Eu which may have peak wavelength at 586 nm, Pb_(0.006)Ca_(0.6)Sr_(0.394)Sb₂O₆: Mn⁴⁺ which may have peak wavelength at about 637 nm, Pb_(0.15)Ba_(1.84)Zn_(0.01)Si_(0.99)Zr_(0.01)O₄: Eu which may have peak wavelength at around 512 nm, and Cu_(0.2)Sr_(3.8)Al₁₄O₂₅: Eu which may have peak wavelength at about 494 nm.

In such an embodiment, part of the initial about 405 nm wavelength emission light from the light emitting diode is absorbed by the phosphor, and it is converted to longer 2^(nd) wavelength. The 1^(st) and 2^(nd) light is mixed together and the desire emission is produced. As the shown FIG. 6, the light emitting device convert the 1^(st) UV light of 405 nm wavelength to wide spectral range of visible light, that is, white light, and at this time the color temperature is about 3,000K and CRI is about 90 to about 95.

FIG. 7 is another embodiment's emission spectrum, which the phosphor is applied for the light emitting device. The embodiment may have a light emitting diode with about 455 nm wavelength and the phosphor, which is mixture of the selected multiple chemical compounds in proper ratio.

The phosphor is composed of Cu_(0.05)Sr_(1.7)Ca_(0.25)SiO₄: Eu which may have peak wavelength at about 592 nm, Pb_(0.1)Ba_(0.95)Sr_(0.95)Si_(0.998)Ge_(0.002)O₄: Eu which may have peak wavelength at about 527 nm, and Cu_(0.05)Li_(0.002)Sr_(1.5)Ba_(0.448)SiO₄: Gd, Eu which may have peak wavelength at about 557 nm.

In such an embodiment, part of the initial about 455 nm wavelength emission light from the light emitting diode is absorbed by the phosphor, and it is converted to longer 2^(nd) wavelength. The 1^(st) and 2^(nd) light is mixed together and the desire emission is produced. As the shown FIG. 7, the light emitting device convert the 1st blue light of about 455 nm wavelength to wide spectral range of visible light, that is, white light, and at this time the color temperature is about 4,000K to about 6,500K and CRI is about 86 to about 93.

The phosphor of the light emitting device exemplarily described herein can be applied by single chemical compound or mixture of plurality of single chemical compound besides the embodiments in relation to FIG. 6 and FIG. 7, which are explained above.

According to the description above, light emitting device with wide range of color temperature about 2,000K to about 8,000K or about 10,000K and superior color rendering index of greater than about 60 (e.g., between about 60 and about 90, or greater than about 90, or between about 90 and about 95) can be realized by using the lead- and/or copper-containing chemical compounds.

In such a wavelength conversion, the light emitting device exemplarily described herein is capable of use in mobile phones, note book computers and electronic devices such as home appliance, stereo, telecommunication products, as well as in custom display's key pad and back light applications. Moreover, the light emitting device exemplarily described herein can be applied in automobiles, medical instruments and illumination products.

In addition, the chemical compounds exemplarily described herein can be incorporated within paint as a pigment capable of converting wavelengths of light.

According to the embodiments exemplarily described above, the chemical can increase the stability of the light emitting device against water, humidity, vapor as well as other polar solvents.

In the foregoing described embodiments, various features are grouped together in a single embodiment for purposes of streamlining the disclosure. This method of disclosure is not to be interpreted as reflecting an intention that the claimed invention requires more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive aspects lie in less than all features of a single foregoing disclosed embodiment. Thus, the following claims are hereby incorporated into this Detailed Description, with each claim standing on its own as a separate preferred embodiment of the invention. 

What is claimed is:
 1. A light emitting device, comprising: a light emitting diode to emit light; and a phosphor to change a wavelength of the light, the phosphor covering at least a portion of the light emitting diode, the phosphor comprising: a compound comprising a host lattice and a luminescent ion, the luminescent ion comprising at least one rare earth element within the host lattice, wherein the host lattice comprises first ions and oxygen, wherein a portion of the first ions are substituted by copper ions, wherein the compound is to emit light upon excitation with ultraviolet light or visible light, due to direct-type transitions, f-d transitions, or charge transfer transitions, wherein the luminescent ion does not comprise copper, and wherein the compound has the formula: a(M′O).b(M″₂O) .c(M″X) .4-a-b-c(M′″O) .7(Al₂O₃) .d(B₂O₃) .e(Ga₂O₃) .f(SiO₂) .g(GeO₂) .h(M″″_(x)O_(y)), wherein: M′ is Cu or a combination of Cu and Pb; M″ is Li, Na, K, Rb, Cs, Au, Ag, or any combination thereof; M′″ is Be, Mg, Ca, Sr, Ba, Zn, Cd, Mn, or any combination thereof; M″″ is Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, or any combination thereof, or is at least one of Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, and Yb in combination with at least one of Bi, Sn, Sb, Sc, Y, La, Ce, In, and Lu; X is F, CI, Br, I, or any combination thereof; 0<a≦4; 0≦b≦2; 0≦c≦2; 0≦d≦1; 0≦e≦1; 0≦f≦1; 0≦g≦1; 0<h≦2; 1≦x≦2; and 0≦y≦5.
 2. A light emitting device, comprising: a light emitting diode to emit light; and a phosphor to change a wavelength of the light, the phosphor covering at least a portion of the light emitting diode, the phosphor comprising: a compound comprising a host lattice and a luminescent ion, the luminescent ion comprising at least one rare earth element within the host lattice, wherein the host lattice comprises first ions and oxygen, wherein a portion of the first ions are substituted by copper ions, wherein the compound is to emit light upon excitation with ultraviolet light or visible light, due to direct-type transitions, f-d transitions, or charge transfer transitions, wherein the luminescent ion does not comprise copper, and wherein the compound has the formula: a(M′O) .b(M″O) .c(Al₂O₃) .d(M′″₂O₃) .e(M″″O₂) .f(M′″″_(x)O_(y)), wherein: M′ is Cu or a combination of Cu and Pb; M″ is Be, Mg, Ca, Sr, Ba, Zn, Cd, Mn, or any combination of thereof; M′″ is B, Ga, ln, or any combination thereof; M″″ is Si, Ge, Ti, Zr, Hf, or any combination thereof; M′″″ is Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, or any combination thereof, or is at least one of Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, and Yb in combination with at least one of Sc, Y, La, Ce, and Lu; 0<a≦1; 0≦b≦2; 0<c≦8; 0≦d≦1; 0≦e≦1; 0<f≦2; 1≦x≦2; and 1≦y≦5.
 3. A light emitting device, comprising: a light emitting diode to emit light; and a phosphor to change a wavelength of the light, the phosphor covering at least a portion of the light emitting diode, the phosphor comprising: a compound comprising a host lattice and a luminescent ion, the luminescent ion comprising at least one rare earth element within the host lattice, wherein the host lattice comprises first ions and oxygen, wherein a portion of the first ions are substituted by copper ions, wherein the compound is to emit light upon excitation with ultraviolet light or visible light, due to direct-type transitions, f-d transitions, or charge transfer transitions, wherein the luminescent ion does not comprise copper, and wherein the compound has the formula: a(M′O) .b(M″₂O) .c(M″X) .d(Sb₂O₅) .e(M′″O) .f(M″″_(x)O_(y)), wherein: M′ is Cu or a combination of Cu and Pb; M″ is Li, Na, K, Rb, Cs, Au, Ag, or any combination thereof; M′″ is Be, Mg, Ca, Sr, Ba, Zn, Cd, Mn, or any combination thereof; M″″ is Pr, Sm, Eu, Tb, Dy, Gd, or any combination thereof, or is at least one of Pr, Sm, Eu, Gd, Tb, and Dy in combination with at least one of Bi, Sn, Sc, Y, and La; X is F, CI, Br, I, or any combination thereof; 0<a≦1; 0≦b≦2; 0≦c≦4; 0<d≦8; 0≦e≦8; 0≦f≦2; 1≦x≦2; and 1≦y≦5.
 4. The light emitting device of claim 1, wherein the divalent copper ions are to increase luminous density of the phosphor.
 5. The light emitting device of claim 2, wherein the divalent copper ions are to increase luminous density of the phosphor.
 6. The light emitting device of claim 3, wherein the divalent copper ions are to increase luminous density of the phosphor. 